Tensile bond strength of two ceramic and three resin composite inlay materials placed using a resin luting agent. 1995

M Thordrup, and F Isidor, and G Ravnholt

Department of Prosthetic Dentistry and Stomatognathic Physiology, Royal Dental College, University of Aarhus, Denmark.

The tensile bond strength of inlay materials to dentin was evaluated. Five materials, two direct resin composite inlay products, one hybrid resin composite, a preformed ceramic block, and a conventional porcelain material were bonded to bovine dentin and bonded together using a dual-polymerizing resin luting agent. Specimens were tested with and without thermocycling. Some bar-to-bar bonding groups fractured through the bar. Significantly higher (P < .05) bar-to-bar bonds were recorded than the bar-dentin bonds, irrespective of the inlay materials. VitaDur N showed the lowest bar-to-bar failure values (7.6 MPa) compared to the four other inlay materials (14.4 MPa to 22.2 MPa), but had the highest dentin bond strength (4.5 MPa). Unexpectedly, thermal loading increased the bond strength to bovine dentin, although this was only statistically significant for VitaDur N. The dentin bond strength of Charisma (1.4 MPa) was inferior (P < .02) to all other materials (2.6 MPa to 4.5 MPa) when thermocycled before testing.

UI	MeSH Term	Description	Entries
D007284	Inlays	Restorations of metal, porcelain, or plastic made to fit a cavity preparation, then cemented into the tooth. Onlays are restorations which fit into cavity preparations and overlay the occlusal surface of a tooth or teeth. Onlays are retained by frictional or mechanical factors.	Dental Inlays,Dental Onlays,Onlays,Dental Inlay,Dental Onlay,Inlay, Dental,Inlays, Dental,Onlay, Dental,Onlays, Dental,Inlay,Onlay
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D011109	Polymethacrylic Acids	Poly-2-methylpropenoic acids. Used in the manufacture of methacrylate resins and plastics in the form of pellets and granules, as absorbent for biological materials and as filters; also as biological membranes and as hydrogens. Synonyms: methylacrylate polymer; poly(methylacrylate); acrylic acid methyl ester polymer.	Methacrylic Acid Polymers,Acid Polymers, Methacrylic,Acids, Polymethacrylic,Polymers, Methacrylic Acid
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002417	Cattle	Domesticated bovine animals of the genus Bos, usually kept on a farm or ranch and used for the production of meat or dairy products or for heavy labor.	Beef Cow,Bos grunniens,Bos indicus,Bos indicus Cattle,Bos taurus,Cow,Cow, Domestic,Dairy Cow,Holstein Cow,Indicine Cattle,Taurine Cattle,Taurus Cattle,Yak,Zebu,Beef Cows,Bos indicus Cattles,Cattle, Bos indicus,Cattle, Indicine,Cattle, Taurine,Cattle, Taurus,Cattles, Bos indicus,Cattles, Indicine,Cattles, Taurine,Cattles, Taurus,Cow, Beef,Cow, Dairy,Cow, Holstein,Cows,Dairy Cows,Domestic Cow,Domestic Cows,Indicine Cattles,Taurine Cattles,Taurus Cattles,Yaks,Zebus
D002516	Ceramics	Products made by baking or firing nonmetallic minerals (clay and similar materials). In making dental restorations or parts of restorations the material is fused porcelain. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed & Boucher's Clinical Dental Terminology, 4th ed)	Ceramic
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003776	Dental Porcelain	A type of porcelain used in dental restorations, either jacket crowns or inlays, artificial teeth, or metal-ceramic crowns. It is essentially a mixture of particles of feldspar and quartz, the feldspar melting first and providing a glass matrix for the quartz. Dental porcelain is produced by mixing ceramic powder (a mixture of quartz, kaolin, pigments, opacifiers, a suitable flux, and other substances) with distilled water. (From Jablonski's Dictionary of Dentistry, 1992)	Porcelain,Porcelain, Dental,Dental Porcelains,Porcelains,Porcelains, Dental
D005976	Glutaral	One of the protein CROSS-LINKING REAGENTS that is used as a disinfectant for sterilization of heat-sensitive equipment and as a laboratory reagent, especially as a fixative.	Glutaraldehyde,Cidex,Diswart,Gludesin,Glutardialdehyde,Glutarol,Korsolex,Novaruca,Sekumatic,Sonacide,Sporicidin
D000537	Aluminum Oxide	An oxide of aluminum, occurring in nature as various minerals such as bauxite, corundum, etc. It is used as an adsorbent, desiccating agent, and catalyst, and in the manufacture of dental cements and refractories.	Alumina,Alumina Ceramic,Aluminum Oxide (Al130O40),Aluminum Oxide (Al2O),Aluminum Oxide (AlO2),Bauxite,Corundum,Sapphire,Ceramic, Alumina,Oxide, Aluminum