This study evaluated the effect of two dentin disinfectants (Consepsis, Tubulicid), one aqueous HEMA solution (Aqua Prep), a combination of Aqua Prep and Tubulicid and an air abrasion treatment (50 microns aluminum oxide) on the shear bond strength (SBS) of two acetone-based single bottle adhesives (One Step and Prime & Bond 2.1). The occlusal surfaces of 167 freshly extracted human third molars were ground flat to expose the dentin, then polished with a 600 grit-polishing disc. The teeth were randomly assigned to 12 test groups (two bonding agents, six pretreatment protocols). The exposed dentin was etched with 35% phosphoric acid for 20 seconds, rinsed and briefly (1-2 seconds) air dried. Six pretreatment protocols were then applied. The air abrasion groups were exceptional, as etching was carried out only after pretreatment. One Step, or Prime & Bond 2.1 was applied according to the manufacturer's instructions. Cylinders of Z-100 composite were bonded to the flat dentin surfaces by transparent gelatin capsules. Specimens were thermocycled in water baths between 5 degrees and 55 degrees C, then sheared in an Instron Testing Machine. One-way and two-way ANOVA and Tukey HSD post-hoc tests were used for statistical analysis. In the One Step group, Consepsis yielded a significantly higher SBS (17.8 MPa) than air abrasion (9.5 MPa), Control (11.8 MPa) and Aqua Prep + Tubilicid (11.9 MPa), and a comparable SBS with Tubilicid (12.5 MPa) and Aqua Prep (14.8 MPa). In the Prime & Bond 2.1 group, Aqua Prep (24.9 MPa) showed a significantly higher SBS than all other groups: air abrasion (9.3 MPa), Control (9.97 MPa), Tubilicid (12.2 MPa), Consepsis (13.0 MPa) and Tubilicid + Aqua Prep (13.3 MPa).