Localized wear of compomer restorative materials. 2001

M A Latta, and W W Barkmeier, and T M Wilwerding, and S M Blake

Department of General Dentistry, Creighton University School of Dentistry, Center for Oral Health Research, Omaha NE 68178, USA. mlatta@creighton.edu

OBJECTIVE To determine and compare the localized wear of six compomer restorative materials. METHODS Ten specimens of Dyract, Dyract AP, F2000, Compoglass F, Elan and Hytac were prepared in a custom fixture and polished. A pretest surface profile was generated using an MTS 3-D surface profilometer and the specimens were subjected to 400,000 cycles in a Leinfelder wear machine equipped with a conical stylus tip to simulate localized wear. A post-test profile was generated and the before and after profiles were fitted and analyzed using AnSur 3-D software. The total volume loss and depth of the wear facet on each specimen was calculated and statistical analysis was accomplished (ANOVA and Tukey's test). RESULTS Volume loss (mm3) was as follows: F2000, 0.027 +/- 0.002; Hytac, 0.007 +/- 0.023; Elan, 0.054 +/- 0.013; Compoglass F, 0.135 +/- 0.006; Dyract AP, 0.135 +/- 0.023; Dyract, 0.185 +/- 0.032. Maximum depth of the wear facets (microm) was as follows: F2000, 112.2 +/- 10.2; Hytac, 132.8 +/- 9.3; Elan, 144.3 +/- 23. 1; Compoglass F, 168.3 +/- 13.0; Dyract AP, 194.0 +/- 19.7; Dyract, 220.6 +/- 15.8. There was not a difference (P > 0.05) in volumetric loss between F2000 and Hytac or between Hytac and Elan. The volume loss and maximum depth of the wear facets of F2000, Hytac and Elan was significantly less (P< 0.05) than Compoglass F, Dyract AP and Dyract The results of this study indicate that there are significant differences in the in vitro wear rates of compomer materials.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008689	Methacrylates	Acrylic acids or acrylates which are substituted in the C-2 position with a methyl group.	Methacrylate
D008963	Molar	The most posterior teeth on either side of the jaw, totaling eight in the deciduous dentition (2 on each side, upper and lower), and usually 12 in the permanent dentition (three on each side, upper and lower). They are grinding teeth, having large crowns and broad chewing surfaces. (Jablonski, Dictionary of Dentistry, 1992, p821)	Molars
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D000704	Analysis of Variance	A statistical technique that isolates and assesses the contributions of categorical independent variables to variation in the mean of a continuous dependent variable.	ANOVA,Analysis, Variance,Variance Analysis,Analyses, Variance,Variance Analyses
D001641	Bicuspid	One of the eight permanent teeth, two on either side in each jaw, between the canines (CUSPID) and the molars (MOLAR), serving for grinding and crushing food. The upper have two cusps (bicuspid) but the lower have one to three. (Jablonski, Dictionary of Dentistry, 1992, p822)	Premolar,Bicuspids,Premolars
D017640	Silicates	The generic term for salts derived from silica or the silicic acids. They contain silicon, oxygen, and one or more metals, and may contain hydrogen. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th Ed)	Silicate
D018709	Statistics, Nonparametric	A class of statistical methods applicable to a large set of probability distributions used to test for correlation, location, independence, etc. In most nonparametric statistical tests, the original scores or observations are replaced by another variable containing less information. An important class of nonparametric tests employs the ordinal properties of the data. Another class of tests uses information about whether an observation is above or below some fixed value such as the median, and a third class is based on the frequency of the occurrence of runs in the data. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed, p1284; Corsini, Concise Encyclopedia of Psychology, 1987, p764-5)	Kolmogorov-Smirnov Test,Kruskal-Wallis H Statistic,Mann-Whitney U Test,Rank-Sum Tests,Spearman Rank Correlation Coefficient,Wilcox Test,Wilcoxon Rank Test,Non-Parametric Statistics,Nonparametric Statistics,Statistics, Non-Parametric,Kolmogorov Smirnov Test,Mann Whitney U Test,Non Parametric Statistics,Rank Sum Tests,Rank Test, Wilcoxon,Rank-Sum Test,Statistics, Non Parametric,Test, Kolmogorov-Smirnov,Test, Mann-Whitney U,Test, Rank-Sum,Test, Wilcox,Test, Wilcoxon Rank,Tests, Rank-Sum,U Test, Mann-Whitney
D019554	Dental Restoration Wear	Occlusal wear of the surfaces of restorations and surface wear of dentures.	Denture Wear,Occlusal Wear, Restoration,Restoration Occlusal Wear,Restoration Wear, Dental,Wear, Dental Restoration,Wear, Restoration Occlusal,Wear, Denture