Bond strength of composites to etched and silica-coated porcelain fusing alloys. 1992

W Schneider, and J M Powers, and H P Pierpont

University of Texas Health Science Center at Houston, Dental Branch.

In vitro bond strengths of two composite veneering materials to two porcelain fusing alloys were measured utilizing two storage conditions. The alloys were etched or treated with silica applied by blasted, thermal or pyrogenic techniques and then silanated. Bond strengths were higher for the Ni-Cr-Be than the Au-Pd alloy with most values greater than 18 MPa. Bond strengths to etched and silanated Au-Pd alloy were low (less than 6.5 MPa), whereas samples treated with silica and silanated had significantly higher values. Bond strengths to the Ni-Cr-Be alloy were highest with the thermal and pyrogenic silica treatments. After thermocycling, most bond strengths to the Au-Pd alloy decreased, but were the same or higher to the Ni-Cr-Be alloy. Cohesive failures of the opaquers were observed.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002858	Chromium Alloys	Specific alloys not less than 85% chromium and nickel or cobalt, with traces of either nickel or cobalt, molybdenum, and other substances. They are used in partial dentures, orthopedic implants, etc.	Chromium-Cobalt Alloys,Chromium-Nickel Alloys,Cobalt-Chromium Alloys,Nickel-Chromium Alloys,Alloys, Chromium,Alloys, Chromium-Cobalt,Alloys, Chromium-Nickel,Alloys, Cobalt-Chromium,Alloys, Nickel-Chromium,Chromium Cobalt Alloys,Chromium Nickel Alloys,Cobalt Chromium Alloys,Nickel Chromium Alloys
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003776	Dental Porcelain	A type of porcelain used in dental restorations, either jacket crowns or inlays, artificial teeth, or metal-ceramic crowns. It is essentially a mixture of particles of feldspar and quartz, the feldspar melting first and providing a glass matrix for the quartz. Dental porcelain is produced by mixing ceramic powder (a mixture of quartz, kaolin, pigments, opacifiers, a suitable flux, and other substances) with distilled water. (From Jablonski's Dictionary of Dentistry, 1992)	Porcelain,Porcelain, Dental,Dental Porcelains,Porcelains,Porcelains, Dental
D006047	Gold Alloys	Alloys that contain a high percentage of gold. They are used in restorative or prosthetic dentistry.	Gold Alloy,Alloy, Gold,Alloys, Gold
D000704	Analysis of Variance	A statistical technique that isolates and assesses the contributions of categorical independent variables to variation in the mean of a continuous dependent variable.	ANOVA,Analysis, Variance,Variance Analysis,Analyses, Variance,Variance Analyses
D012821	Silanes	Compounds similar to hydrocarbons in which a tetravalent silicon atom replaces the carbon atom. They are very reactive, ignite in air, and form useful derivatives.	Silane
D012822	Silicon Dioxide	Transparent, tasteless crystals found in nature as agate, amethyst, chalcedony, cristobalite, flint, sand, QUARTZ, and tridymite. The compound is insoluble in water or acids except hydrofluoric acid.	Silica,Aerosil,Aerosil 380,Cristobalite,Quso G-32,Quso G32,Tridymite,380, Aerosil,Dioxide, Silicon,G32, Quso,Quso G 32
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property