Film thickness of new adhesive luting agents. 1992

S N White, and Z Yu

Department of Restorative Dentistry, University of Southern California, School of Dentistry, Los Angeles.

This study determined and compared the film thicknesses of new adhesive luting agents. The method was in compliance with American National Standards Institution/American Dental Association (ADA) Specification No. 8 for zinc phosphate cement. Each of the 20 materials tested was manipulated exactly as described in the manufacturers' instructions. An electronic gauge with an accuracy of 0.5 micron was recalibrated after each recording, and each luting agent was measured 10 times. The mean film thickness and standard deviation were calculated for each luting agent; an analysis of variance and a multiple comparison test were also performed. Nine materials satisfied the ADA type I specification for film thicknesses less than 25 microns, and these included a hydroxyapatite cement, glass ionomer cements, zinc phosphate cements, and polycarboxylate cements. Five other materials met the ADA type II specification for film thicknesses of less than 40 microns, and these included a glass ionomer cement, a resinous cement, a zinc phosphate cement, and glass ionomer-resinous hybrids. Six resinous cements recorded film thicknesses greater than 40 microns, and suggestions were made regarding future development and research.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D011076	Polycarboxylate Cement	Water-soluble low-molecular-weight polymers of acrylic or methacrylic acid that form solid, insoluble products when mixed with specially prepared ZnO powder. The resulting cement adheres to dental enamel and is also used as a luting agent.	Zinc Polycarboxylate Cement,Cement, Polycarboxylate,Cement, Zinc Polycarboxylate,Polycarboxylate Cement, Zinc
D012117	Resins, Synthetic	Polymers of high molecular weight which at some stage are capable of being molded and then harden to form useful components.	Dental Resins,Dental Resin,Resin, Dental,Resin, Synthetic,Resins, Dental,Synthetic Resin,Synthetic Resins
D003738	Dental Cements	Substances used to bond COMPOSITE RESINS to DENTAL ENAMEL and DENTIN. These bonding or luting agents are used in restorative dentistry, ROOT CANAL THERAPY; PROSTHODONTICS; and ORTHODONTICS.	Dental Adhesives,Luting Agents,Orthodontic Adhesives,Cement, Dental,Cements, Dental,Dental Cement,Adhesive, Dental,Adhesive, Orthodontic,Adhesives, Dental,Adhesives, Orthodontic,Dental Adhesive,Luting Agent,Orthodontic Adhesive
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D006882	Hydroxyapatites	A group of compounds with the general formula M10(PO4)6(OH)2, where M is barium, strontium, or calcium. The compounds are the principal mineral in phosphorite deposits, biological tissue, human bones, and teeth. They are also used as an anticaking agent and polymer catalysts. (Grant & Hackh's Chemical Dictionary, 5th ed)	Hydroxyapatite Derivatives,Derivatives, Hydroxyapatite
D000269	Adhesives	Substances that cause the adherence of two surfaces. They include glues (properly collagen-derived adhesives), mucilages, sticky pastes, gums, resins, or latex.	Glues,Mucilage Adhesive,Mucilage Adhesives,Mucilages, Adhesive,Adhesive,Adhesive Mucilage,Adhesive Mucilages,Adhesive, Mucilage,Adhesives, Mucilage,Glue,Mucilage, Adhesive
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property
D015036	Zinc Phosphate Cement	A material used for cementation of inlays, crowns, bridges, and orthodontic appliances and occasionally as a temporary restoration. It is prepared by mixing zinc oxide and magnesium oxide powders with a liquid consisting principally of phosphoric acid, water, and buffers. (From Bouchers' Clinical Dental Terminology, 3d ed)	Cement, Zinc Phosphate
D017886	Durapatite	The mineral component of bones and teeth; it has been used therapeutically as a prosthetic aid and in the prevention and treatment of osteoporosis.	Calcium Hydroxyapatite,Hydroxyapatite,Hydroxylapatite,Alveograf,Calcitite,Interpore-200,Interpore-500,Osprovit,Ossein-Hydroxyapatite Compound,Ossopan,Osteogen,Periograf,Hydroxyapatite, Calcium,Interpore 200,Interpore 500,Interpore200,Interpore500,Ossein Hydroxyapatite Compound