Effects of dentin surface treatments on the shear bond strength of Vitrabond. 1992

C Prati, and G Montanari, and G Biagini, and F Fava, and D H Pashley

School of Dentistry, Medical College of Georgia.

The influences of nine dentin surface treatments were evaluated on the shear bond strength of a new light-cured glass-ionomer cement (GIC) and on the SEM morphology of the treated dentin surfaces. The following treatments were performed: saline solution (control), NaOCl, acidic glycine, EDTA, malic acid, malic acid plus glycine, polyacrylic acid, tannic acid, and neutral+acidic oxalate solutions. Buccal dentin surfaces were polished with #320-grit abrasive paper, treated with one of the chemicals, washed, and air-dried. Cylindrical GIC samples were then applied to the dentin surface, stored in 100% humidity, and tested after 24 h. SEM observations demonstrated no effect of saline or NaOCl treatment on the smear layer but its complete removal with exposure of collagen fibrils after malic or malic acid plus glycine treatment. Partial removal of the smear layer occurred following glycine treatment and with tannic or polyacrylic acids. Complete removal of the smear layer was seen after EDTA or pyruvic acid treatment. Oxalate treatment produced a layer of crystals, which completely covered the dentin surface. Shear bond strength of GIC was significantly increased only by treatment with the oxalate solutions.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property
D013501	Surface-Active Agents	Agents that modify interfacial tension of water; usually substances that have one lipophilic and one hydrophilic group in the molecule; includes soaps, detergents, emulsifiers, dispersing and wetting agents, and several groups of antiseptics.	Surface Active Agent,Surface-Active Agent,Surfactant,Surfactants,Tenside,Amphiphilic Agents,Surface Active Agents,Tensides,Active Agent, Surface,Active Agents, Surface,Agent, Surface Active,Agent, Surface-Active,Agents, Amphiphilic,Agents, Surface Active,Agents, Surface-Active
D013718	Tensile Strength	The maximum stress a material subjected to a stretching load can withstand without tearing. (McGraw-Hill Dictionary of Scientific and Technical Terms, 5th ed, p2001)	Strength, Tensile,Strengths, Tensile,Tensile Strengths