Biomaterial Database

Surface roughness of flowable and packable composite resin materials after finishing with abrasive discs. 2004

M B Uçtaşli, and O Bala, and A Güllü

Department of Operative Dentistry, Faculty of Dentistry, University of Gazi, Ankara, Turkey. uctasli@gazi.edu.tr

The aim of this study was to compare surface roughness of flowable (Admira Flow, Filtek Flow, Tetric Flow) and packable (Admira, Filtek P60, Tetric HB) composite resin restorative materials finishing with Sof-Lex discs by means of average surface roughness (Ra) measurement using a surface profilometer and scanning electron microscopy (SEM). For each test group five specimens were prepared and roughness was measured in five different positions using a profilometer with a traversing distance of 4 mm and a cut-off value of 0.8 mm. The radius of the tracing diamond tip was 5 microm and measuring force and speed was 4 mN and 0.5 mm/s, respectively. The surface roughness of each individual disk was taken as the arithmetic mean of the Ra values measured in five different positions. Additionally, one specimen of each test group after finishing was observed under SEM with the magnification of x800 and x2500. Before finishing with Sof-Lex discs, flowable composite materials showed a smoother surface than packable composites restoratives (P < 0.05). However, after the finishing procedures similar surface textures were observed both from packable and flowable composites (P > 0.05).

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003775	Dental Polishing	Creation of a smooth and glossy surface finish on a denture or amalgam.	Dental Burnishing,Dental Finishing,Burnishing, Dental,Finishing, Dental,Polishing, Dental
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property