Comparison of temperature changes in the pulp chamber induced by various light curing units, in vitro. 2006

A Rüya Yazici, and Ali Müftü, and Gerard Kugel, and Ronald D Perry

Hacettepe University, Faculty of Dentistry, Department of Conservative Dentistry, Ankara, Turkey. ruyay@hacettepe.edu.tr

This study compared the temperature increase in a pulp chamber as a result of using various light-curing units during resin composite polymerization, and it determined the effect of remaining dentin thickness on temperature rise. A Class II occlusodistal cavity with a remaining dentin thickness of 2 mm was prepared in an extracted human mandibular molar. A 2-mm layer of fine hybrid resin composite was placed on the floor of the proximal box. A K-type thermocouple was inserted into pulp chambers filled with heat sink compound, and pulp chamber temperature rise (starting temperature: 37.0 +/- 0.1 degrees C) during polymerization of the composite was measured. The light-curing units tested included two halogen lights, Spectrum 800 and Elipar Trilight (Standard and Exponential mode); a light-emitting diode (LED, Elipar Freelight) and a plasma arc (Virtuoso, Xenon Power Arc). Irradiation time was 40 seconds for the halogen and LED lights and 3 seconds for the plasma arc light. Five measurements were carried out for every light-curing unit. The same experimental design was conducted after the cavity preparation was modified, leaving a 1-mm thick dentin layer. The Kruskal-Wallis and multiple comparison tests were used to evaluate the differences among the tested curing units. Mann Whitney-U tests were used to compare the mean temperature rise in each curing unit for different remaining dentin thicknesses. The increase in pulp chamber temperature ranged between 1.40-3.8 degrees C. The highest temperature rise was observed when using Elipar Trilight Standard mode, and the lowest temperature rise was observed with light emitting diode for both remaining dentin thicknesses. The only significant differences in temperature rise were observed between Elipar Trilight Standard mode and LED. No significant difference (p > 0.01) existed for the different modes of Elipar Trilight. A statistically significant higher temperature rise was observed within each curing unit at a depth of 1 mm compared to 2 mm. Although the tested light-curing units caused a temperature rise in the pulp chamber, none exceed the critical value of 5.5 degrees C.

UI	MeSH Term	Description	Entries
D008027	Light	That portion of the electromagnetic spectrum in the visible, ultraviolet, and infrared range.	Light, Visible,Photoradiation,Radiation, Visible,Visible Radiation,Photoradiations,Radiations, Visible,Visible Light,Visible Radiations
D011140	Polyurethanes	A group of thermoplastic or thermosetting polymers containing polyisocyanate. They are used as ELASTOMERS, as coatings, as fibers and as foams.	Polyisocyanates,Ostamer,Pellethane,Spandex,Ostamers,Pellethanes,Polyisocyanate,Polyurethane,Spandices
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003786	Dental Pulp Cavity	The space in a tooth bounded by the dentin and containing the dental pulp. The portion of the cavity within the crown of the tooth is the pulp chamber; the portion within the root is the pulp canal or root canal.	Pulp Canal,Pulp Chamber,Root Canal,Cavities, Dental Pulp,Cavity, Dental Pulp,Dental Pulp Cavities,Pulp Cavities, Dental,Pulp Cavity, Dental,Canal, Pulp,Canal, Root,Canals, Pulp,Canals, Root,Chamber, Pulp,Chambers, Pulp,Pulp Canals,Pulp Chambers,Root Canals
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins
D006219	Halogens	A family of nonmetallic, generally electronegative, elements that form group 17 (formerly group VIIa) of the periodic table.	Halogen,Group 17 Elements,Elements, Group 17
D006358	Hot Temperature	Presence of warmth or heat or a temperature notably higher than an accustomed norm.	Heat,Hot Temperatures,Temperature, Hot,Temperatures, Hot
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000180	Acrylic Resins	Polymers of high molecular weight which are derived from acrylic acid, methacrylic acid or other related compounds and are capable of being molded and then hardened to form useful components.	Acrylic Resin,Resin, Acrylic,Resins, Acrylic
D018709	Statistics, Nonparametric	A class of statistical methods applicable to a large set of probability distributions used to test for correlation, location, independence, etc. In most nonparametric statistical tests, the original scores or observations are replaced by another variable containing less information. An important class of nonparametric tests employs the ordinal properties of the data. Another class of tests uses information about whether an observation is above or below some fixed value such as the median, and a third class is based on the frequency of the occurrence of runs in the data. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed, p1284; Corsini, Concise Encyclopedia of Psychology, 1987, p764-5)	Kolmogorov-Smirnov Test,Kruskal-Wallis H Statistic,Mann-Whitney U Test,Rank-Sum Tests,Spearman Rank Correlation Coefficient,Wilcox Test,Wilcoxon Rank Test,Non-Parametric Statistics,Nonparametric Statistics,Statistics, Non-Parametric,Kolmogorov Smirnov Test,Mann Whitney U Test,Non Parametric Statistics,Rank Sum Tests,Rank Test, Wilcoxon,Rank-Sum Test,Statistics, Non Parametric,Test, Kolmogorov-Smirnov,Test, Mann-Whitney U,Test, Rank-Sum,Test, Wilcox,Test, Wilcoxon Rank,Tests, Rank-Sum,U Test, Mann-Whitney