Tensile strength of five types of retention for resin-bonded prostheses. 1991

M T Bastos, and J Mondelli, and A Ishikiriama, and M F Navarro

Department of Operative Dentistry, University of São Paulo, Dental School of Bauru, Brazil.

The tensile bond strengths of five retention techniques for bonded cast restorations were tested. The retentive methods were the electrolytic etch, Rochette's perforations, retention beads, the recessed surface, and soldered orthodontic mesh. The electrolytic etch and recessed surface methods gave the highest values of bond strength, followed by retention beads. Rochette's perforations and the soldered orthodontic mesh failed to surpass the bond strength of the control group (no additional retention) after 1 hour and provided the lowest bond strength after 24 hours.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D009566	Nitrates	Inorganic or organic salts and esters of nitric acid. These compounds contain the NO3- radical.	Nitrate
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002858	Chromium Alloys	Specific alloys not less than 85% chromium and nickel or cobalt, with traces of either nickel or cobalt, molybdenum, and other substances. They are used in partial dentures, orthopedic implants, etc.	Chromium-Cobalt Alloys,Chromium-Nickel Alloys,Cobalt-Chromium Alloys,Nickel-Chromium Alloys,Alloys, Chromium,Alloys, Chromium-Cobalt,Alloys, Chromium-Nickel,Alloys, Cobalt-Chromium,Alloys, Nickel-Chromium,Chromium Cobalt Alloys,Chromium Nickel Alloys,Cobalt Chromium Alloys,Nickel Chromium Alloys
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003779	Denture Design	The plan, delineation, and location of actual structural elements of dentures. The design can relate to retainers, stress-breakers, occlusal rests, flanges, framework, lingual or palatal bars, reciprocal arms, etc.	Denture Designs,Design, Denture,Designs, Denture
D003781	Denture Retention	The retention of a denture in place by design, device, or adhesion.	Denture Stability,Retention, Denture,Stability, Denture
D004572	Electrolysis	Destruction by passage of a galvanic electric current, as in disintegration of a chemical compound in solution.	Electrolyses
D000134	Acid Etching, Dental	Preparation of TOOTH surfaces and DENTAL MATERIALS with etching agents, usually phosphoric acid, to roughen the surface to increase adhesion or osteointegration.	Dental Acid Etching,Etching, Dental Acid
D000180	Acrylic Resins	Polymers of high molecular weight which are derived from acrylic acid, methacrylic acid or other related compounds and are capable of being molded and then hardened to form useful components.	Acrylic Resin,Resin, Acrylic,Resins, Acrylic