Amelogenesis imperfecta (AI) comprises a diverse group of hereditary enamel disorders that are characterized by hypoplastic and in some cases hypomineralized defects. The specific biochemical abnormalities remain unknown for all AI types, making histologic and chemical analyses of affected dentitions essential for resolving the etiology of AI. The purpose of this investigation was to characterize the ultrastructure and mineral content of smooth hypoplastic AI enamel. The AI enamel showed no evidence of surface pitting and was uniformly reduced in thickness by approximately 60% compared with control enamel. Imbibition studies indicated that the AI enamel was generally porous. The first 30 microns of AI enamel adjacent to the dentinoenamel junction was translucent with poorly formed prisms. Abnormal prism structure was seen throughout the AI enamel. Amorphous, presumably organic material that may have been retained enamel protein was also seen. Although the crystallite widths were similar in both AI and normal enamel, the AI teeth showed areas where the crystallite order and continuity appeared disrupted. The mean mineral content was similar for all variables measured except sodium, which was significantly lower in the AI teeth. The calcium concentration was very low in the AI enamel directly adjacent to the dentinoenamel junction and showed a steeper concentration gradient moving from the dentin to the surface compared with control teeth. It may be concluded that the ameloblasts in smooth hypoplastic AI produce a tissue of reduced thickness, which is excessively porous and displays alterations in its ultrastructural organization.