In vitro shear bond strength of dentin adhesives. 1991

J A Sorensen, and N V Dixit

School of Dentistry, University of California, Los Angeles.

This in vitro study compared the shear bond strengths of current dentin adhesives. Freshly extracted human molars were prepared to a flat surface and treated with dentin adhesives and composite resin light polymerized in a plastic matrix. Completed samples were stored in 37 degrees C water and thermocycled 1,500 times. Samples were sheared at the tooth/composite resin interface using a wire loop. The reliability index varied significantly between materials. Large coefficients of variation were found for all dentin adhesives. One dentin adhesive was able to achieve a bond strength to dentin that was 47% of the control bond strength of enamel.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D009566	Nitrates	Inorganic or organic salts and esters of nitric acid. These compounds contain the NO3- radical.	Nitrate
D010070	Oxalates	Derivatives of OXALIC ACID. Included under this heading are a broad variety of acid forms, salts, esters, and amides that are derived from the ethanedioic acid structure.	Oxalate,Ethanedioic Acids,Oxalic Acids,Acids, Ethanedioic,Acids, Oxalic
D011109	Polymethacrylic Acids	Poly-2-methylpropenoic acids. Used in the manufacture of methacrylate resins and plastics in the form of pellets and granules, as absorbent for biological materials and as filters; also as biological membranes and as hydrogens. Synonyms: methylacrylate polymer; poly(methylacrylate); acrylic acid methyl ester polymer.	Methacrylic Acid Polymers,Acid Polymers, Methacrylic,Acids, Polymethacrylic,Polymers, Methacrylic Acid
D011140	Polyurethanes	A group of thermoplastic or thermosetting polymers containing polyisocyanate. They are used as ELASTOMERS, as coatings, as fibers and as foams.	Polyisocyanates,Ostamer,Pellethane,Spandex,Ostamers,Pellethanes,Polyisocyanate,Polyurethane,Spandices
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003738	Dental Cements	Substances used to bond COMPOSITE RESINS to DENTAL ENAMEL and DENTIN. These bonding or luting agents are used in restorative dentistry, ROOT CANAL THERAPY; PROSTHODONTICS; and ORTHODONTICS.	Dental Adhesives,Luting Agents,Orthodontic Adhesives,Cement, Dental,Cements, Dental,Dental Cement,Adhesive, Dental,Adhesive, Orthodontic,Adhesives, Dental,Adhesives, Orthodontic,Dental Adhesive,Luting Agent,Orthodontic Adhesive
D003743	Dental Enamel	A hard thin translucent layer of calcified substance which envelops and protects the dentin of the crown of the tooth. It is the hardest substance in the body and is almost entirely composed of calcium salts. Under the microscope, it is composed of thin rods (enamel prisms) held together by cementing substance, and surrounded by an enamel sheath. (From Jablonski, Dictionary of Dentistry, 1992, p286)	Enamel,Enamel Cuticle,Dental Enamels,Enamel, Dental,Enamels, Dental,Cuticle, Enamel,Cuticles, Enamel,Enamel Cuticles,Enamels
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins