Repairability of type II glass polyalkenoate (ionomer) cements. 1991

D G Charlton, and D F Murchison, and B K Moore

Department of Dental Materials, Indiana University School of Dentistry, Indianapolis.

Two Type II glass polyalkenoate (ionomer) cements were evaluated for their repairability by measuring tensile bond strength of new material added to previously placed cement. Variables included time of repair (20 min vs. 24 h) and surface condition prior to repair (smooth and unetched, smooth and etched, rough and unetched, rough and etched). Failures were evaluated using light microscopy and categorized as cohesive, adhesive, or mixed. Scanning electron microscopy was employed to view the cement surfaces following each of the four pretreatments. Surface pretreatment was found to significantly affect both materials when repaired at 20 min (P less than 0.05). The highest bond strength was achieved when bonding to the smooth, unetched surface. Surface pretreatment did not significantly affect bond strength when the cements were repaired at 24 h (P greater than 0.05). Tensile bond strengths were greater for repairs made at 20 min than for those made at 24 h, but the differences were not always statistically significant.

UI	MeSH Term	Description	Entries
D008298	Maleates	Derivatives of maleic acid (the structural formula (COO-)-C
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002244	Carbon	A nonmetallic element with atomic symbol C, atomic number 6, and atomic weight [12.0096; 12.0116]. It may occur as several different allotropes including DIAMOND; CHARCOAL; and GRAPHITE; and as SOOT from incompletely burned fuel.	Carbon-12,Vitreous Carbon,Carbon 12,Carbon, Vitreous
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D000134	Acid Etching, Dental	Preparation of TOOTH surfaces and DENTAL MATERIALS with etching agents, usually phosphoric acid, to roughen the surface to increase adhesion or osteointegration.	Dental Acid Etching,Etching, Dental Acid
D000704	Analysis of Variance	A statistical technique that isolates and assesses the contributions of categorical independent variables to variation in the mean of a continuous dependent variable.	ANOVA,Analysis, Variance,Variance Analysis,Analyses, Variance,Variance Analyses
D012825	Silicon	A trace element that constitutes about 27.6% of the earth's crust in the form of SILICON DIOXIDE. It does not occur free in nature. Silicon has the atomic symbol Si, atomic number 14, and atomic weight [28.084; 28.086].	Silicon-28,Silicon 28
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property