Effect of LED curing modes on the microleakage of a pit and fissure sealant. 2007

Adil Nalçaci, and Nuran Ulusoy, and Ciğem Küçükeşmen

Department of Restorative Dentistry, Faculty of Dentistry, Ankara University, Turkey. analcaci@dentistry.ankara.edu.tr

OBJECTIVE To evaluate in vitro the curing effect of a very high intensity light-emitting diode (LED) unit and a conventional LED unit (including "soft-start" modes) on the microleakage of a pit and fissure sealant. METHODS 120 intact caries-free human molars were randomly divided into six groups (n=20), sealed with Fissurit-F and polymerized using either a conventional halogen unit (Optilux) (Control group) in standard mode (40 seconds @ 600 mW/cm2); a very high intensity LED unit (Mini LED) in fast (10 seconds @ 1,100 mW/cm2) or soft-start mode (pulse mode: ten 1-second flashes @ 1,100 mW/cm2; exponential mode: exponential increase from 0 to 1,100 mW/cm2 within 10 seconds followed by 10 seconds @1,100 mW/cm2); or a conventional LED unit (Elipar Freelight) in standard (40 seconds @ 400 mW/cm2) or exponential mode (exponential increase from 0 to 400mW/cm2 within 12 seconds followed by 28 seconds @ 400 mW/cm2). Restored specimens were stored in distilled water at 37 degrees C for 24 hours. Specimens were then immersed in a 0.5% fuchsin dye solution for 24 hours, with half of the specimens from each group subjected to thermocycling (5/55 degrees C; x 1000) prior to dye immersion. After removal from the dye solution, specimens were sectioned and the degree of dye penetration scored. Data was statistically analyzed using the Kruskal-Wallis H test and the Mann-Whitney U-test (P< 0.05). RESULTS There was no statistically significant difference in microleakage of pit and fissure sealant polymerized using various curing techniques. Thermocycling regimens had no effect on either LED- or halogen-cured specimens.

UI	MeSH Term	Description	Entries
D008963	Molar	The most posterior teeth on either side of the jaw, totaling eight in the deciduous dentition (2 on each side, upper and lower), and usually 12 in the permanent dentition (three on each side, upper and lower). They are grinding teeth, having large crowns and broad chewing surfaces. (Jablonski, Dictionary of Dentistry, 1992, p821)	Molars
D010895	Pit and Fissure Sealants	Agents used to occlude dental enamel pits and fissures in the prevention of dental caries.	Dental Sealant,Dental Sealants,Fissure Sealant,Fissure Sealants,Pit And Fissure Sealant,Pit Fissure Sealant,Sealants, Tooth,Pit Fissure Sealants,Sealants, Dental,Fissure Sealant, Pit,Fissure Sealants, Pit,Sealant, Dental,Sealant, Fissure,Sealant, Pit Fissure,Sealant, Tooth,Sealants, Fissure,Sealants, Pit Fissure,Tooth Sealant,Tooth Sealants
D011140	Polyurethanes	A group of thermoplastic or thermosetting polymers containing polyisocyanate. They are used as ELASTOMERS, as coatings, as fibers and as foams.	Polyisocyanates,Ostamer,Pellethane,Spandex,Ostamers,Pellethanes,Polyisocyanate,Polyurethane,Spandices
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003763	Dental Leakage	The seepage of fluids, debris, and micro-organisms between the walls of a prepared dental cavity and the restoration.	Dental Leakages,Leakage, Dental,Leakages, Dental
D006219	Halogens	A family of nonmetallic, generally electronegative, elements that form group 17 (formerly group VIIa) of the periodic table.	Halogen,Group 17 Elements,Elements, Group 17
D006358	Hot Temperature	Presence of warmth or heat or a temperature notably higher than an accustomed norm.	Heat,Hot Temperatures,Temperature, Hot,Temperatures, Hot
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000180	Acrylic Resins	Polymers of high molecular weight which are derived from acrylic acid, methacrylic acid or other related compounds and are capable of being molded and then hardened to form useful components.	Acrylic Resin,Resin, Acrylic,Resins, Acrylic
D018709	Statistics, Nonparametric	A class of statistical methods applicable to a large set of probability distributions used to test for correlation, location, independence, etc. In most nonparametric statistical tests, the original scores or observations are replaced by another variable containing less information. An important class of nonparametric tests employs the ordinal properties of the data. Another class of tests uses information about whether an observation is above or below some fixed value such as the median, and a third class is based on the frequency of the occurrence of runs in the data. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed, p1284; Corsini, Concise Encyclopedia of Psychology, 1987, p764-5)	Kolmogorov-Smirnov Test,Kruskal-Wallis H Statistic,Mann-Whitney U Test,Rank-Sum Tests,Spearman Rank Correlation Coefficient,Wilcox Test,Wilcoxon Rank Test,Non-Parametric Statistics,Nonparametric Statistics,Statistics, Non-Parametric,Kolmogorov Smirnov Test,Mann Whitney U Test,Non Parametric Statistics,Rank Sum Tests,Rank Test, Wilcoxon,Rank-Sum Test,Statistics, Non Parametric,Test, Kolmogorov-Smirnov,Test, Mann-Whitney U,Test, Rank-Sum,Test, Wilcox,Test, Wilcoxon Rank,Tests, Rank-Sum,U Test, Mann-Whitney