Abrasion of human enamel by different dental ceramics in vitro. 1991

R R Seghi, and S F Rosenstiel, and P Bauer

School of Dentistry, University of California, Los Angeles 90024.

Manufacturers generally quote indentation hardness values when predicting the clinical wear potential of newly introduced ceramic restoratives. The objective of this study was to determine whether in vitro two-body wear correlated well with hardness. A modified polisher was used to abrade enamel cylinders against polished disks of commercially available dental porcelains and glass. Enamel loss after four h was measured with a micrometer. Five ceramic materials were tested, and enamel abrasion rates were correlated with Knoop hardness values. Dicor and Dicor coated with a shading porcelain were found to cause the lowest wear of enamel. These rates were statistically significantly lower than those obtained with Optec, the most abrasive material. These findings may be due to microstructural differences between the materials. Knoop hardness showed poor correlation with the results of the abrasive testing.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D002516	Ceramics	Products made by baking or firing nonmetallic minerals (clay and similar materials). In making dental restorations or parts of restorations the material is fused porcelain. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed & Boucher's Clinical Dental Terminology, 4th ed)	Ceramic
D003743	Dental Enamel	A hard thin translucent layer of calcified substance which envelops and protects the dentin of the crown of the tooth. It is the hardest substance in the body and is almost entirely composed of calcium salts. Under the microscope, it is composed of thin rods (enamel prisms) held together by cementing substance, and surrounded by an enamel sheath. (From Jablonski, Dictionary of Dentistry, 1992, p286)	Enamel,Enamel Cuticle,Dental Enamels,Enamel, Dental,Enamels, Dental,Cuticle, Enamel,Cuticles, Enamel,Enamel Cuticles,Enamels
D003776	Dental Porcelain	A type of porcelain used in dental restorations, either jacket crowns or inlays, artificial teeth, or metal-ceramic crowns. It is essentially a mixture of particles of feldspar and quartz, the feldspar melting first and providing a glass matrix for the quartz. Dental porcelain is produced by mixing ceramic powder (a mixture of quartz, kaolin, pigments, opacifiers, a suitable flux, and other substances) with distilled water. (From Jablonski's Dictionary of Dentistry, 1992)	Porcelain,Porcelain, Dental,Dental Porcelains,Porcelains,Porcelains, Dental
D003793	Dental Restoration, Permanent	A restoration designed to remain in service for not less than 20 to 30 years, usually made of gold casting, cohesive gold, or amalgam. (Jablonski, Dictionary of Dentistry, 1992)	Dental Fillings, Permanent,Dental Filling, Permanent,Dental Permanent Filling,Dental Permanent Fillings,Dental Restorations, Permanent,Filling, Dental Permanent,Filling, Permanent Dental,Fillings, Dental Permanent,Fillings, Permanent Dental,Permanent Dental Filling,Permanent Dental Fillings,Permanent Dental Restoration,Permanent Dental Restorations,Permanent Filling, Dental,Permanent Fillings, Dental,Restoration, Permanent Dental,Restorations, Permanent Dental
D006244	Hardness	The mechanical property of material that determines its resistance to force. HARDNESS TESTS measure this property.	Hardnesses
D006245	Hardness Tests	A test to determine the relative HARDNESS of a metal, mineral, or other material according to one of several scales, such as Brinell, Mohs, Rockwell, Vickers, or Shore. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 6th ed).	Hardness Test,Test, Hardness,Tests, Hardness
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property