The effect of aging on the fracture toughness of esthetic restorative materials. 2010

Rafat Bagheri, and Mohammad R Azar, and Martin J Tyas, and Michael F Burrow

Department of Restorative Dentistry, Dental School, Shiraz University of Medical Science, Shiraz, Iran. bagherir@unimelb.edu.au

OBJECTIVE To compare the fracture toughness (KIc) of tooth-colored restorative materials based on a four-point bending; to assess the effect of distilled water and a resin surface sealant (G-Coat Plus) on the resistance of the materials to fracture. METHODS Specimens were prepared from six materials: Quix Fil; Dyract (Dentsply), Freedom (SDI), Fuji VII (GC), Fuji IX (GC); Fuji II LC (GC). Fuji II LC and Fuji IX were tested both with and without applying G-Coat Plus (GC). The specimens were divided into the three groups which were conditioned in distilled water at 37 degrees C for 48 hours, 4 and 8 weeks. The specimens were loaded in a four-point bending test using a universal testing machine. The maximum load to specimen failure was recorded and the fracture toughness calculated. RESULTS There were significant differences among most of the materials (P < 0.001). Quix Fil had the highest mean KIc value and Fuji VII the lowest. Immersion in distilled water for the resin composite and polyacid-modified resin composites caused a significant decrease in KIc as the time interval increased. For glass-ionomer cements, KIc decreased significantly after 4 weeks, and after 8 weeks immersion slightly increased. G-Coat Plus affected Fuji II LC positively while it had no effect on the Fuji IX.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003793	Dental Restoration, Permanent	A restoration designed to remain in service for not less than 20 to 30 years, usually made of gold casting, cohesive gold, or amalgam. (Jablonski, Dictionary of Dentistry, 1992)	Dental Fillings, Permanent,Dental Filling, Permanent,Dental Permanent Filling,Dental Permanent Fillings,Dental Restorations, Permanent,Filling, Dental Permanent,Filling, Permanent Dental,Fillings, Dental Permanent,Fillings, Permanent Dental,Permanent Dental Filling,Permanent Dental Fillings,Permanent Dental Restoration,Permanent Dental Restorations,Permanent Filling, Dental,Permanent Fillings, Dental,Restoration, Permanent Dental,Restorations, Permanent Dental
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D013997	Time Factors	Elements of limited time intervals, contributing to particular results or situations.	Time Series,Factor, Time,Time Factor
D014867	Water	A clear, odorless, tasteless liquid that is essential for most animal and plant life and is an excellent solvent for many substances. The chemical formula is hydrogen oxide (H2O). (McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed)	Hydrogen Oxide
D018583	Pliability	The quality or state of being able to be bent or creased repeatedly. (From Webster, 3d ed)	Flexibility
D019279	Resin Cements	Dental cements composed either of polymethyl methacrylate or dimethacrylate, produced by mixing an acrylic monomer liquid with acrylic polymers and mineral fillers. The cement is insoluble in water and is thus resistant to fluids in the mouth, but is also irritating to the dental pulp. It is used chiefly as a luting agent for fabricated and temporary restorations. (Jablonski's Dictionary of Dentistry, 1992, p159)	Resin Cement,Cement, Resin,Cements, Resin
D020099	Coated Materials, Biocompatible	Biocompatible materials usually used in dental and bone implants that enhance biologic fixation, thereby increasing the bond strength between the coated material and bone, and minimize possible biological effects that may result from the implant itself.	Surface-Coated Materials,Biocompatible Coated Materials,Materials, Biocompatible Coated,Materials, Surface-Coated,Surface Coated Materials