In vitro resistance to fracture of porcelain inlays bonded to tooth. 1990

D Dietschi, and M Maeder, and J M Meyer, and J Holz

Department of Preventive and Therapeutic Dentistry, University of Geneva, Faculty of Medicine, Switzerland.

To assess the resistance to fracture of ceramic inlays, extracted sound human molars were restored with different ceramic materials and glass-ionomer or composite resin luting cement. Compression forces were applied to the specimens until they fractured, and maximal force developed, extent and location of fractures, and the micromorphology of the fractured surfaces were studied. Inlays made of Vitadur N with aluminum oxide profile and bonded with composite resin demonstrated the highest resistance among the restorative combinations, but their resistance was still lower than that of intact (control) teeth. The extent of fracture increased proportionally to the fracture resistance of the specimens. Scanning electron microscopic observation confirmed the effectiveness of the adhesion between composite resin and etched ceramic and the absence of sufficient micromechanical anchoring between glass-ionomer cement and etched ceramic.

UI	MeSH Term	Description	Entries
D007284	Inlays	Restorations of metal, porcelain, or plastic made to fit a cavity preparation, then cemented into the tooth. Onlays are restorations which fit into cavity preparations and overlay the occlusal surface of a tooth or teeth. Onlays are retained by frictional or mechanical factors.	Dental Inlays,Dental Onlays,Onlays,Dental Inlay,Dental Onlay,Inlay, Dental,Inlays, Dental,Onlay, Dental,Onlays, Dental,Inlay,Onlay
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008964	Molar, Third	The aftermost permanent tooth on each side in the maxilla and mandible.	Tooth, Wisdom,Teeth, Wisdom,Molars, Third,Third Molar,Third Molars,Wisdom Teeth,Wisdom Tooth
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002484	Cementation	The joining of objects by means of a cement (e.g., in fracture fixation, such as in hip arthroplasty for joining of the acetabular component to the femoral component). In dentistry, it is used for the process of attaching parts of a tooth or restorative material to a natural tooth or for the attaching of orthodontic bands to teeth by means of an adhesive.	Cementations
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003776	Dental Porcelain	A type of porcelain used in dental restorations, either jacket crowns or inlays, artificial teeth, or metal-ceramic crowns. It is essentially a mixture of particles of feldspar and quartz, the feldspar melting first and providing a glass matrix for the quartz. Dental porcelain is produced by mixing ceramic powder (a mixture of quartz, kaolin, pigments, opacifiers, a suitable flux, and other substances) with distilled water. (From Jablonski's Dictionary of Dentistry, 1992)	Porcelain,Porcelain, Dental,Dental Porcelains,Porcelains,Porcelains, Dental
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man