Mechanical properties of injection-molded thermoplastic denture base resins. 2011

Ippei Hamanaka, and Yutaka Takahashi, and Hiroshi Shimizu

Division of Removable Prosthodontics, Fukuoka Dental College, Fukuoka, Japan.

OBJECTIVE To investigate the mechanical properties of injection-molded thermoplastic denture base resins. METHODS Four injection-molded thermoplastic resins (two polyamides, one polyethylene terephthalate, one polycarbonate) and, as a control, a conventional heat-polymerized polymethyl methacrylate (PMMA), were used in this study. The flexural strength at the proportional limit (FS-PL), the elastic modulus, and the Charpy impact strength of the denture base resins were measured according to International Organization for Standardization (ISO) 1567 and ISO 1567:1999/Amd 1:2003. RESULTS The descending order of the FS-PL was: conventional PMMA > polyethylene terephthalate, polycarbonate > two polyamides. The descending order of the elastic moduli was: conventional PMMA > polycarbonate > polyethylene terephthalate > two polyamides. The descending order of the Charpy impact strength was: polyamide (Nylon PACM12) > polycarbonate > polyamide (Nylon 12), polyethylene terephthalate > conventional PMMA. CONCLUSIONS All of the injection-molded thermoplastic resins had significantly lower FS-PL, lower elastic moduli, and higher or similar impact strength compared to the conventional PMMA. The polyamide denture base resins had low FS-PL and low elastic moduli; one of them possessed very high impact strength, and the other had low impact strength. The polyethylene terephthalate denture base resin showed a moderately high FS-PL, moderate elastic modulus, and low impact strength. The polycarbonate denture base resin had a moderately high FS-PL, moderately high elastic modulus, and moderate impact strength.

UI	MeSH Term	Description	Entries
D007267	Injections	Introduction of substances into the body using a needle and syringe.	Injectables,Injectable,Injection
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D009757	Nylons	Polymers where the main polymer chain comprises recurring amide groups. These compounds are generally formed from combinations of diamines, diacids, and amino acids and yield fibers, sheeting, or extruded forms used in textiles, gels, filters, sutures, contact lenses, and other biomaterials.	Polyamides,Dermalon,Ethilon,Nylon,Polyamide,Supramid,Dermalons,Ethilons,Supramids
D011076	Polycarboxylate Cement	Water-soluble low-molecular-weight polymers of acrylic or methacrylic acid that form solid, insoluble products when mixed with specially prepared ZnO powder. The resulting cement adheres to dental enamel and is also used as a luting agent.	Zinc Polycarboxylate Cement,Cement, Polycarboxylate,Cement, Zinc Polycarboxylate,Polycarboxylate Cement, Zinc
D011093	Polyethylene Terephthalates	Polyester polymers formed from terephthalic acid or its esters and ethylene glycol. They can be formed into tapes, films or pulled into fibers that are pressed into meshes or woven into fabrics.	Dacron,Nalophan,PET Polymer,Poly(Ethylene Terephtalate),Polyethylene Terephthalate,Tedlar,Dacrons,Nalophans,PET Polymers,Tedlars,Terephthalate, Polyethylene,Terephthalates, Polyethylene
D011108	Polymers	Compounds formed by the joining of smaller, usually repeating, units linked by covalent bonds. These compounds often form large macromolecules (e.g., BIOPOLYMERS; PLASTICS).	Polymer
D012117	Resins, Synthetic	Polymers of high molecular weight which at some stage are capable of being molded and then harden to form useful components.	Dental Resins,Dental Resin,Resin, Dental,Resin, Synthetic,Resins, Dental,Synthetic Resin,Synthetic Resins
D003764	Dental Materials	Materials used in the production of dental bases, restorations, impressions, prostheses, etc.	Dental Material,Material, Dental,Materials, Dental
D003819	Denture Bases	The part of a denture that overlies the soft tissue and supports the supplied teeth and is supported in turn by abutment teeth or the residual alveolar ridge. It is usually made of resins or metal or their combination.	Base, Denture,Bases, Denture,Denture Base
D006244	Hardness	The mechanical property of material that determines its resistance to force. HARDNESS TESTS measure this property.	Hardnesses