Adhesive bonding of titanium with a titanate coupler and 4-META/MMA-TBB opaque resin. 1990

H Matsumura, and K Yoshida, and T Tanaka, and M Atsuta

Department of Fixed Prosthodontics, Nagasaki University School of Dentistry, Japan.

Adhesive bonding of titanium was evaluated with a titanate primer and adhesive opaque resin. The primer consisted of 2% isopropyl dimethacryloyl isostearoyl titanate in methyl methacrylate. The adhesive was 4-META/MMA-TBB opaque resin that contained 4-methacryloyloxyethyl trimellitate anhydride and was initiated by tri-n-butylborane derivative. Titanium discs were machined and blasted with aluminum oxide. They were primed and bonded together with the opaque resin. A shear test was performed after repeated thermocycles for investigation of the durability of the bond. The shear strength of the primed and 4-META resin-bonded specimens was 37.2 MPa after 50,000 thermocycles, with only a small decrease in bond strength. This was significantly higher than the control values. Thus, titanate primer and 4-META/MMA-TBB opaque resin may be used for the bonding of titanium in prosthodontic practice.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008689	Methacrylates	Acrylic acids or acrylates which are substituted in the C-2 position with a methyl group.	Methacrylate
D008768	Methylmethacrylates	The methyl esters of methacrylic acid that polymerize easily and are used as tissue cements, dental materials, and absorbent for biological substances.
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D001896	Boron Compounds	Inorganic or organic compounds that contain boron as an integral part of the molecule.	Borides,Compounds, Boron
D005069	Evaluation Studies as Topic	Works about studies that determine the effectiveness or value of processes, personnel, and equipment, or the material on conducting such studies.	Critique,Evaluation Indexes,Evaluation Methodology,Evaluation Report,Evaluation Research,Methodology, Evaluation,Pre-Post Tests,Qualitative Evaluation,Quantitative Evaluation,Theoretical Effectiveness,Use-Effectiveness,Critiques,Effectiveness, Theoretical,Evaluation Methodologies,Evaluation Reports,Evaluation, Qualitative,Evaluation, Quantitative,Evaluations, Qualitative,Evaluations, Quantitative,Indexes, Evaluation,Methodologies, Evaluation,Pre Post Tests,Pre-Post Test,Qualitative Evaluations,Quantitative Evaluations,Report, Evaluation,Reports, Evaluation,Research, Evaluation,Test, Pre-Post,Tests, Pre-Post,Use Effectiveness
D006358	Hot Temperature	Presence of warmth or heat or a temperature notably higher than an accustomed norm.	Heat,Hot Temperatures,Temperature, Hot,Temperatures, Hot
D000179	Acrylates	Derivatives of acrylic acid (the structural formula CH2
D000180	Acrylic Resins	Polymers of high molecular weight which are derived from acrylic acid, methacrylic acid or other related compounds and are capable of being molded and then hardened to form useful components.	Acrylic Resin,Resin, Acrylic,Resins, Acrylic
D000269	Adhesives	Substances that cause the adherence of two surfaces. They include glues (properly collagen-derived adhesives), mucilages, sticky pastes, gums, resins, or latex.	Glues,Mucilage Adhesive,Mucilage Adhesives,Mucilages, Adhesive,Adhesive,Adhesive Mucilage,Adhesive Mucilages,Adhesive, Mucilage,Adhesives, Mucilage,Glue,Mucilage, Adhesive