As an initial step in the development of a method for corneal cryopreservation by vitrification, we attempted to establish the maximum concentration of glycerol to which human corneal endothelium could be exposed at 4 degrees C for 15 min without damage. Damage was defined as an increase in mean endothelial cell size or the inability to maintain corneal thickness for 1 week after exposure to glycerol. Using a system for long-term corneal perfusion, we perfused 24 paired human corneas with glycerol at 4 degrees C. The concentration of glycerol increased at a rate of 20% (w/v) (2.2 M) per hour until the desired maximum concentration was reached for that cornea, stabilized for 15 min, and then decreased at the same rate. The corneas were then perfused at 37 degrees C with Dulbecco's medium at a rate of 5 microliters/min under 18 mm Hg intracameral pressure for 7 days with daily measurements of corneal thickness. Endothelial morphology was examined by specular microscopy and by scanning electron microscopy. After 7 days of perfusion at 37 degrees C, there was a statistically significant direct relationship between the maximum concentration of glycerol to which the experimental eyes had been exposed and the increase in mean endothelial cell size. The mean endothelial cell size increased in corneas exposed to glycerol concentrations of 40, 50, and 60% (w/v), but did not differ significantly from baseline measurements in the corneas exposed to 30% glycerol or less. Thus, there was no detectable damage to human corneas exposed to 30% (w/v) (3.3 M) glycerol in this system. Tolerance of higher concentrations may be achieved by changes in the rates of addition and removal of glycerol or in the composition of the perfusate.