[Effect of different sandblasting conditions on the metal-ceramic bonding strength of Co-Cr alloy fabricated by selective laser melting technology]. 2018

Qian-Qian Yu, and Jing Guo, and Hong-Shui Zhu

First Outpatient Department, Nanjing Stomatological Hospital, Medical School of Nanjing University, Nanjing 210008, China.

OBJECTIVE To investigate the effect of different sandblasting conditions on the metal-ceramic bonding strength of Co-Cr alloy fabricated by selective laser melting (SLM) technology. METHODS A total of 63 specimens of Co-Cr alloy fabricated by SLM were prepared and randomly divided into nine groups (n=7). Each group was treated with different powder particles (A1=50 µm, A2=100 µm, and A3=150 µm) and pressures (B1=0.2 MPa, B2=0.4 MPa, and B3=0.6 MPa) in sandblasting. One sample was randomly selected from each group for microstructure observation by scanning electron microscope (SEM). Ceramic was fired at the center of the specimens. Metal-ceramic bonding strength was measured with universal testing machine. Results were statistically analyzed with SPSS 17.0 software. RESULTS The mean bond strengths were as follows: Group A1B1: 27.22 MPa±0.95 MPa, Group A1B2: 27.58 MPa±0.47 MPa, Group A1B3: 26.80 MPa±0.71 MPa, Group A2B1: 27.54 MPa±0.78 MPa, Group A2B2: 30.75 MPa±0.43 MPa, Group A2B3: 26.93 MPa±0.88 MPa, Group A3B1: 28.18 MPa±0.93 MPa, Group A3B2: 29.55 MPa±0.57 MPa, and Group A3B3: 28.11 MPa±0.91 MPa. The particle factor of Al₂O₃ and the pressure factor of blasting showed statistical significance (P<0.05). An interaction was observed between the factors of particle and pressure (P<0.05). Mixed fracture mode of all specimens was observed after the shear strength test. CONCLUSIONS In conclusion, metal-ceramic bonding strength reaches the maximum when specimens are sandblasted with 100 µm alumina oxide at 0.4 MPa pressure.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002516	Ceramics	Products made by baking or firing nonmetallic minerals (clay and similar materials). In making dental restorations or parts of restorations the material is fused porcelain. (From McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed & Boucher's Clinical Dental Terminology, 4th ed)	Ceramic
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property
D033081	Shear Strength	The internal resistance of a material to moving some parts of it parallel to a fixed plane, in contrast to stretching (TENSILE STRENGTH) or compression (COMPRESSIVE STRENGTH). Ionic crystals are brittle because, when subjected to shear, ions of the same charge are brought next to each other, which causes repulsion.	Strength, Shear