The relationship of weight loss to surface roughness of composite resins from simulated toothbrushing. 1982

J Kanter, and R E Koski, and D Martin

This study was designed to measure percentage of weight loss during simulated toothbrushing of five different composite resins. The surface roughness of each composite resin was also measured after each year of simulated toothbrushing for a period of 5 years. The following conclusions were reached: 1. Despite the loss of toothbrush efficiency, all composite resins tested tended to have a decreasing wear rate with the increasing time of toothbrushing. 2. Profile (with a soft filler) and Isopast (with a microsized filler) showed the greatest resistance to abrasion and retained the smoothest surface. 3. Prestige, which demonstrated the greatest percent weight loss, also has a soft barium filler. Loss of the filler as an alkaline reaction in water due to soluble barium compounds may cause the binder to release filler particles prematurely.

UI	MeSH Term	Description	Entries
D008768	Methylmethacrylates	The methyl esters of methacrylic acid that polymerize easily and are used as tissue cements, dental materials, and absorbent for biological substances.
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D011140	Polyurethanes	A group of thermoplastic or thermosetting polymers containing polyisocyanate. They are used as ELASTOMERS, as coatings, as fibers and as foams.	Polyisocyanates,Ostamer,Pellethane,Spandex,Ostamers,Pellethanes,Polyisocyanate,Polyurethane,Spandices
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D000180	Acrylic Resins	Polymers of high molecular weight which are derived from acrylic acid, methacrylic acid or other related compounds and are capable of being molded and then hardened to form useful components.	Acrylic Resin,Resin, Acrylic,Resins, Acrylic
D013499	Surface Properties	Characteristics or attributes of the outer boundaries of objects, including molecules.	Properties, Surface,Property, Surface,Surface Property
D013997	Time Factors	Elements of limited time intervals, contributing to particular results or situations.	Time Series,Factor, Time,Time Factor
D014099	Toothbrushing	The act of cleaning teeth with a brush to remove plaque and prevent tooth decay. (From Webster, 3d ed)	Toothbrushings
D017438	Bisphenol A-Glycidyl Methacrylate	The reaction product of bisphenol A and glycidyl methacrylate that undergoes polymerization when exposed to ultraviolet light or mixed with a catalyst. It is used as a bond implant material and as the resin component of dental sealants and composite restorative materials.	Bis-GMA,Bis-GMA Polymer,2-Propenoic acid, 2-methyl-, (1-methylethylidene)bis(4,1-phenyleneoxy(2-hydroxy-3,1-propanediyl)) ester, homopolymer,Adaptic,Bis(Phenol A-Glycidyl Methacrylate),Bis(Phenol A-Glycidyl Methacrylate), Homopolymer,Bis(Phenol A-Glycydyl Methacrylate),Bis-GMA Resin,Bisphenol A-Glycidyl Methacrylate Homopolymer,Bisphenol A-Glycidyl Methacrylate Polymer,Concise Composite Resin,Concise Enamel Bond,Concise Enamel Bond System,Concise Resin,Concise White Sealant,Conclude Composite Resin,Conclude Resin,Delton,Epoxylite-9075,Kerr Pit and Fissure Sealant,Kerr Sealer,Nuva-Seal,Panavia Opaque,Poly(Bis-GMA),Retroplast,Silux,Bis GMA,Bis GMA Polymer,Bis GMA Resin,Bis-GMA Polymers,Bis-GMA Resins,Bisphenol A Glycidyl Methacrylate,Bisphenol A Glycidyl Methacrylate Homopolymer,Bisphenol A Glycidyl Methacrylate Polymer,Bond, Concise Enamel,Composite Resin, Concise,Composite Resin, Conclude,Composite Resins, Concise,Concise Composite Resins,Concise Resins,Enamel Bond, Concise,Epoxylite 9075,Epoxylite9075,Methacrylate, Bisphenol A-Glycidyl,Nuva Seal,NuvaSeal,Opaque, Panavia,Polymer, Bis-GMA,Polymers, Bis-GMA,Resin, Bis-GMA,Resin, Concise,Resin, Concise Composite,Resin, Conclude,Resin, Conclude Composite,Resins, Bis-GMA,Resins, Concise,Resins, Concise Composite