Resin bonding to primary teeth using three adhesive systems. 1995

N Mazzeo, and N W Ott, and S O Hondrum

Dental Branch Clinic, Naval Base, Keflavik, Iceland.

In vitro bond strengths of three resin adhesive systems were tested using 111 primary teeth. Ninety-six flat dentin surface specimens were divided into six groups consisting of 16 primed or 16 unprimed samples for each adhesive system. The remaining 15 tooth samples were divided into three groups of five to determine each adhesive system's bond strength to primary etched enamel. Resin buttons were polymerized to all specimens with visible light, thermocycled for 2000 cycles between 5 and 55 degrees C, and shear bond strength was measured with a Instron Testing Machine (Instron Engineering Corp, Canton, MA). ANOVA and multiple comparison tests showed that Optibond Multiuse Bonding Agent had a statistically greater mean shear bond strength to primary dentin (20.5 +/- 3.5 MPa) than Prisma Universal Bond 3 Multi-purpose Bonding System (9.1 +/- 4.4 MPa), Scotchbond Multi-purpose Dental Adhesive System (7.3 +/- 3.7 MPa), and primary etched enamel (9.8 +/- 4.4 MPa) at P < 0.05. This study demonstrated that resin adhesive systems may achieve bond strengths to primary dentin comparable to those of primary enamel, and that these bonds may be as strong as bonds to permanent enamel and dentin. These adhesive systems may allow more confident esthetic restoration of primary anterior teeth.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003743	Dental Enamel	A hard thin translucent layer of calcified substance which envelops and protects the dentin of the crown of the tooth. It is the hardest substance in the body and is almost entirely composed of calcium salts. Under the microscope, it is composed of thin rods (enamel prisms) held together by cementing substance, and surrounded by an enamel sheath. (From Jablonski, Dictionary of Dentistry, 1992, p286)	Enamel,Enamel Cuticle,Dental Enamels,Enamel, Dental,Enamels, Dental,Cuticle, Enamel,Cuticles, Enamel,Enamel Cuticles,Enamels
D003793	Dental Restoration, Permanent	A restoration designed to remain in service for not less than 20 to 30 years, usually made of gold casting, cohesive gold, or amalgam. (Jablonski, Dictionary of Dentistry, 1992)	Dental Fillings, Permanent,Dental Filling, Permanent,Dental Permanent Filling,Dental Permanent Fillings,Dental Restorations, Permanent,Filling, Dental Permanent,Filling, Permanent Dental,Fillings, Dental Permanent,Fillings, Permanent Dental,Permanent Dental Filling,Permanent Dental Fillings,Permanent Dental Restoration,Permanent Dental Restorations,Permanent Filling, Dental,Permanent Fillings, Dental,Restoration, Permanent Dental,Restorations, Permanent Dental
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000134	Acid Etching, Dental	Preparation of TOOTH surfaces and DENTAL MATERIALS with etching agents, usually phosphoric acid, to roughen the surface to increase adhesion or osteointegration.	Dental Acid Etching,Etching, Dental Acid
D000269	Adhesives	Substances that cause the adherence of two surfaces. They include glues (properly collagen-derived adhesives), mucilages, sticky pastes, gums, resins, or latex.	Glues,Mucilage Adhesive,Mucilage Adhesives,Mucilages, Adhesive,Adhesive,Adhesive Mucilage,Adhesive Mucilages,Adhesive, Mucilage,Adhesives, Mucilage,Glue,Mucilage, Adhesive