The effect of dentin primer on the tensile bond strength to human enamel. 1994

L M Thoms, and J I Nicholls, and J S Brudvik, and W L Kydd

University of Seattle, Washington.

Four third-generation dentin bonding products (Scotchbond Multi-Purpose, Optibond, All-Bond 2, and Prisma Universal Bond 3) were tested to evaluate their tensile bond strength to enamel. Test enamel specimens were etched, primed, and polymerized according to each manufacturer's directions. Control specimens were treated identically except the primer application was eliminated. The results demonstrated that the dentin primer significantly increased the tensile bond strength of All-Bond 2, significantly decreased the tensile bond strength of Scotchbond Multi-Purpose and Optibond, and had no significant effect for Prisma Universal Bond 3. A one-way analysis of variance was run between the eight groups tested, and three significant subsets were found (P < .05). The subset with the highest mean tensile bond strengths consisted of Prisma Universal Bond 3 primed and nonprimed, All-Bond 2 primed, and Optibond nonprimed.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008689	Methacrylates	Acrylic acids or acrylates which are substituted in the C-2 position with a methyl group.	Methacrylate
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000704	Analysis of Variance	A statistical technique that isolates and assesses the contributions of categorical independent variables to variation in the mean of a continuous dependent variable.	ANOVA,Analysis, Variance,Variance Analysis,Analyses, Variance,Variance Analyses
D013718	Tensile Strength	The maximum stress a material subjected to a stretching load can withstand without tearing. (McGraw-Hill Dictionary of Scientific and Technical Terms, 5th ed, p2001)	Strength, Tensile,Strengths, Tensile,Tensile Strengths
D017220	Dentin-Bonding Agents	Cements that act through infiltration and polymerization within the dentinal matrix and are used for dental restoration. They can be adhesive resins themselves, adhesion-promoting monomers, or polymerization initiators that act in concert with other agents to form a dentin-bonding system.	Dentin Bonding Agent,Dentin-Bonding Agent,Bonding Agents, Dentin,Agent, Dentin Bonding,Agent, Dentin-Bonding,Agents, Dentin Bonding,Agents, Dentin-Bonding,Bonding Agent, Dentin,Dentin Bonding Agents
D017438	Bisphenol A-Glycidyl Methacrylate	The reaction product of bisphenol A and glycidyl methacrylate that undergoes polymerization when exposed to ultraviolet light or mixed with a catalyst. It is used as a bond implant material and as the resin component of dental sealants and composite restorative materials.	Bis-GMA,Bis-GMA Polymer,2-Propenoic acid, 2-methyl-, (1-methylethylidene)bis(4,1-phenyleneoxy(2-hydroxy-3,1-propanediyl)) ester, homopolymer,Adaptic,Bis(Phenol A-Glycidyl Methacrylate),Bis(Phenol A-Glycidyl Methacrylate), Homopolymer,Bis(Phenol A-Glycydyl Methacrylate),Bis-GMA Resin,Bisphenol A-Glycidyl Methacrylate Homopolymer,Bisphenol A-Glycidyl Methacrylate Polymer,Concise Composite Resin,Concise Enamel Bond,Concise Enamel Bond System,Concise Resin,Concise White Sealant,Conclude Composite Resin,Conclude Resin,Delton,Epoxylite-9075,Kerr Pit and Fissure Sealant,Kerr Sealer,Nuva-Seal,Panavia Opaque,Poly(Bis-GMA),Retroplast,Silux,Bis GMA,Bis GMA Polymer,Bis GMA Resin,Bis-GMA Polymers,Bis-GMA Resins,Bisphenol A Glycidyl Methacrylate,Bisphenol A Glycidyl Methacrylate Homopolymer,Bisphenol A Glycidyl Methacrylate Polymer,Bond, Concise Enamel,Composite Resin, Concise,Composite Resin, Conclude,Composite Resins, Concise,Concise Composite Resins,Concise Resins,Enamel Bond, Concise,Epoxylite 9075,Epoxylite9075,Methacrylate, Bisphenol A-Glycidyl,Nuva Seal,NuvaSeal,Opaque, Panavia,Polymer, Bis-GMA,Polymers, Bis-GMA,Resin, Bis-GMA,Resin, Concise,Resin, Concise Composite,Resin, Conclude,Resin, Conclude Composite,Resins, Bis-GMA,Resins, Concise,Resins, Concise Composite
D019279	Resin Cements	Dental cements composed either of polymethyl methacrylate or dimethacrylate, produced by mixing an acrylic monomer liquid with acrylic polymers and mineral fillers. The cement is insoluble in water and is thus resistant to fluids in the mouth, but is also irritating to the dental pulp. It is used chiefly as a luting agent for fabricated and temporary restorations. (Jablonski's Dictionary of Dentistry, 1992, p159)	Resin Cement,Cement, Resin,Cements, Resin