Failure strength of four veneered primary stainless steel crowns. 1995

W F Waggoner, and H Cohen

Ohio State University, Columbus, USA.

The purpose of this study was to determine the amount of shear force required to fracture or dislodge the veneered facings of four commercially available veneered primary incisor stainless steel crowns (SSC) and to characterize the veneer failures. Forty Unitek SSCs (#4 left central incisor) were shaped to fit a master die and then 10 each were mailed to four commercial dental laboratories that produce veneered SSCs. The resulting four types of crowns tested were: Cheng Crowns (CC), [Peter Cheng Orthodontic Laboratory]; Kinder Krowns (KK) [Mayclin Dental Studio, Inc]; NuSmile Primary Crowns (NC), [Orthodontic Technologies, Inc]; and Whiter Biter Crown II (WB), [White Bite Inc]. Each crown was cemented onto a standardized die and then thermocycled at 4 degrees C and 55 degrees C for 500 1-min cycles. Each die was then placed into a custom holder on the Instron (Model 4204) testing machine. A force was applied at the incisal edge of the veneer at 148 degrees, (the primary inter-incisal angle), with a crosshead speed of 1 mm/min until the veneer fractured or was dislodged. The mean force (N) required +/- SD to produce failure was, respectively: KK (397.2 +/- 53.0); NC (447.2 +/- 78.5); CC (511.9 +/- 83.4); WB (686.5 +/- 181.4). Analysis of variance (ANOVA) indicated significance at P < 0.0001. A Scheffe's post hoc comparison demonstrated that the Whiter Biter (WB) group required significantly (alpha = 0.05) more force for failure than the other three groups.(ABSTRACT TRUNCATED AT 250 WORDS)

UI	MeSH Term	Description	Entries
D007180	Incisor	Any of the eight frontal teeth (four maxillary and four mandibular) having a sharp incisal edge for cutting food and a single root, which occurs in man both as a deciduous and a permanent tooth. (Jablonski, Dictionary of Dentistry, 1992, p820)	Incisors
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008768	Methylmethacrylates	The methyl esters of methacrylic acid that polymerize easily and are used as tissue cements, dental materials, and absorbent for biological substances.
D010969	Plastics	Polymeric materials (usually organic) of large molecular weight which can be shaped by flow. Plastic usually refers to the final product with fillers, plasticizers, pigments, and stabilizers included (versus the resin, the homogeneous polymeric starting material). (McGraw-Hill Dictionary of Scientific and Technical Terms, 4th ed)	Plastic
D011475	Prosthesis Failure	Malfunction of implantation shunts, valves, etc., and prosthesis loosening, migration, and breaking.	Prosthesis Loosening,Prosthesis Durability,Prosthesis Migration,Prosthesis Survival,Durabilities, Prosthesis,Durability, Prosthesis,Failure, Prosthesis,Failures, Prosthesis,Loosening, Prosthesis,Loosenings, Prosthesis,Migration, Prosthesis,Migrations, Prosthesis,Prosthesis Durabilities,Prosthesis Failures,Prosthesis Loosenings,Prosthesis Migrations,Prosthesis Survivals,Survival, Prosthesis,Survivals, Prosthesis
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003188	Composite Resins	Synthetic resins, containing an inert filler, that are widely used in dentistry.	Composite Resin,Resin, Composite,Resins, Composite
D003442	Crowns	A prosthetic restoration that reproduces the entire surface anatomy of the visible natural crown of a tooth. It may be partial (covering three or more surfaces of a tooth) or complete (covering all surfaces). It is made of gold or other metal, porcelain, or resin.	Dental Crowns,Crown, Dental,Crowns, Dental,Dental Crown,Crown
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D003801	Dental Veneers	The use of a layer of tooth-colored material, usually porcelain or acrylic resin, applied to the surface of natural teeth, crowns, or pontics by fusion, cementation, or mechanical retention.	Dental Laminates,Dental Laminate,Dental Veneer,Laminate, Dental,Laminates, Dental,Veneer, Dental,Veneers, Dental