Biomaterial Database

Diametral tensile strength and bonding to dentin of type I glass ionomer cements. 1994

E A Galun, and N Saleh, and I Lewinstein

Laboratory for Biomaterials, Hebrew University-Hadassah School of Dental Medicine, Jerusalem, Israel.

This study evaluated the diametral tensile strength of type I glass ionomer cements and measured their tensile and shear bond strengths to dentin with and without conditioning. Four brands of glass ionomer cement and one brand of zinc phosphate cement were tested. Disks of each cement type were prepared and the 7-day diametral compression test for tension was conducted. The shear and tensile tests, with and without 10% polyacrylic acid dentin conditioning, were performed with an Instron testing machine. Two additional groups, one for each bond test, were prepared and conditioned with 90% trichloracetic acid. No significant differences of the diametral strength were found among the various glass ionomer cements. The comparison of means suggests that, except for trichloracetic acid dentin pretreatment, the conditioning is an effective promoter of shear strength and has no significant effect (p < 0.01) on the tensile bond strength. However, trichloracetic acid was found to be a most effective dentin conditioner for both shear and tensile bond strengths (p < 0.01).

UI	MeSH Term	Description	Entries
D008277	Magnesium Oxide	Magnesium oxide (MgO). An inorganic compound that occurs in nature as the mineral periclase. In aqueous media combines quickly with water to form magnesium hydroxide. It is used as an antacid and mild laxative and has many nonmedicinal uses.	Magnesia,Oxide, Magnesium
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D011076	Polycarboxylate Cement	Water-soluble low-molecular-weight polymers of acrylic or methacrylic acid that form solid, insoluble products when mixed with specially prepared ZnO powder. The resulting cement adheres to dental enamel and is also used as a luting agent.	Zinc Polycarboxylate Cement,Cement, Polycarboxylate,Cement, Zinc Polycarboxylate,Polycarboxylate Cement, Zinc
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins
D005069	Evaluation Studies as Topic	Works about studies that determine the effectiveness or value of processes, personnel, and equipment, or the material on conducting such studies.	Critique,Evaluation Indexes,Evaluation Methodology,Evaluation Report,Evaluation Research,Methodology, Evaluation,Pre-Post Tests,Qualitative Evaluation,Quantitative Evaluation,Theoretical Effectiveness,Use-Effectiveness,Critiques,Effectiveness, Theoretical,Evaluation Methodologies,Evaluation Reports,Evaluation, Qualitative,Evaluation, Quantitative,Evaluations, Qualitative,Evaluations, Quantitative,Indexes, Evaluation,Methodologies, Evaluation,Pre Post Tests,Pre-Post Test,Qualitative Evaluations,Quantitative Evaluations,Report, Evaluation,Reports, Evaluation,Research, Evaluation,Test, Pre-Post,Tests, Pre-Post,Use Effectiveness
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000134	Acid Etching, Dental	Preparation of TOOTH surfaces and DENTAL MATERIALS with etching agents, usually phosphoric acid, to roughen the surface to increase adhesion or osteointegration.	Dental Acid Etching,Etching, Dental Acid