Effect of surface treatment on shear bond strength of zirconia to human dentin. 2011

John Chai, and Frederick C S Chu, and Tak W Chow

Northwestern University, Evanston, IL, USA.

OBJECTIVE The effect of surface treatment using tribochemical silica coating/silane coupling on the shear bond strengths of (1) a glass-infiltrated, zirconia-reinforced alumina (In-Ceram Zirconia) and (2) a yttria-stabilized zirconia ceramic (YZ Zirconia) to human dentin was studied. METHODS Twelve specimens of each ceramic were randomly assigned to one of three surface treatments: (1) no surface treatment (control group); (2) a chairside tribochemical silica coating/silane coupling system (CoJet group); and (3) a laboratory tribochemical silica coating/silane coupling system (Rocatac group). The mode of failure of each specimen was determined under magnification. RESULTS The shear bond strengths (mean ± SD) of In-Ceram Zirconia of the control, CoJet and Rocatec groups were 5.7 ± 4.3 MPa, 11.4 ± 5.4 MPa, and 6.5 ± 4.8 MPa, respectively. The corresponding figures for YZ Zirconia were 8.2 ± 5.4 MPa, 9.8 ± 5.4 MPa, and 7.8 ± 4.7 MPa. Two-way ANOVA revealed significant differences in bond strength due to the difference in surface treatment (p= 0.02), but the bond strengths between the two ceramics were not significantly different (p= 0.56). Post hoc tests showed that In-Ceram Zirconia treated with CoJet had significantly higher shear bond strengths than those untreated (p < 0.05) or treated with Rocatec (p < 0.05). Surface treatment did not affect the shear bond strength of YZ Zirconia significantly (p > 0.05). CONCLUSIONS The bonding of In-Ceram Zirconia can be improved by the chairside surface treatment system.

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008855	Microscopy, Electron, Scanning	Microscopy in which the object is examined directly by an electron beam scanning the specimen point-by-point. The image is constructed by detecting the products of specimen interactions that are projected above the plane of the sample, such as backscattered electrons. Although SCANNING TRANSMISSION ELECTRON MICROSCOPY also scans the specimen point by point with the electron beam, the image is constructed by detecting the electrons, or their interaction products that are transmitted through the sample plane, so that is a form of TRANSMISSION ELECTRON MICROSCOPY.	Scanning Electron Microscopy,Electron Scanning Microscopy,Electron Microscopies, Scanning,Electron Microscopy, Scanning,Electron Scanning Microscopies,Microscopies, Electron Scanning,Microscopies, Scanning Electron,Microscopy, Electron Scanning,Microscopy, Scanning Electron,Scanning Electron Microscopies,Scanning Microscopies, Electron,Scanning Microscopy, Electron
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D002484	Cementation	The joining of objects by means of a cement (e.g., in fracture fixation, such as in hip arthroplasty for joining of the acetabular component to the femoral component). In dentistry, it is used for the process of attaching parts of a tooth or restorative material to a natural tooth or for the attaching of orthodontic bands to teeth by means of an adhesive.	Cementations
D003738	Dental Cements	Substances used to bond COMPOSITE RESINS to DENTAL ENAMEL and DENTIN. These bonding or luting agents are used in restorative dentistry, ROOT CANAL THERAPY; PROSTHODONTICS; and ORTHODONTICS.	Dental Adhesives,Luting Agents,Orthodontic Adhesives,Cement, Dental,Cements, Dental,Dental Cement,Adhesive, Dental,Adhesive, Orthodontic,Adhesives, Dental,Adhesives, Orthodontic,Dental Adhesive,Luting Agent,Orthodontic Adhesive
D003776	Dental Porcelain	A type of porcelain used in dental restorations, either jacket crowns or inlays, artificial teeth, or metal-ceramic crowns. It is essentially a mixture of particles of feldspar and quartz, the feldspar melting first and providing a glass matrix for the quartz. Dental porcelain is produced by mixing ceramic powder (a mixture of quartz, kaolin, pigments, opacifiers, a suitable flux, and other substances) with distilled water. (From Jablonski's Dictionary of Dentistry, 1992)	Porcelain,Porcelain, Dental,Dental Porcelains,Porcelains,Porcelains, Dental
D003799	Dental Stress Analysis	The description and measurement of the various factors that produce physical stress upon dental restorations, prostheses, or appliances, materials associated with them, or the natural oral structures.	Analyses, Dental Stress,Analysis, Dental Stress,Stress Analyses, Dental,Stress Analysis, Dental,Dental Stress Analyses
D003804	Dentin	The hard portion of the tooth surrounding the pulp, covered by enamel on the crown and cementum on the root, which is harder and denser than bone but softer than enamel, and is thus readily abraded when left unprotected. (From Jablonski, Dictionary of Dentistry, 1992)	Dentine,Dentines,Dentins
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000537	Aluminum Oxide	An oxide of aluminum, occurring in nature as various minerals such as bauxite, corundum, etc. It is used as an adsorbent, desiccating agent, and catalyst, and in the manufacture of dental cements and refractories.	Alumina,Alumina Ceramic,Aluminum Oxide (Al130O40),Aluminum Oxide (Al2O),Aluminum Oxide (AlO2),Bauxite,Corundum,Sapphire,Ceramic, Alumina,Oxide, Aluminum