The effect of air abrasion on shear bond strength to dentin with dental adhesives. 1997

P J Rinaudo, and M A Cochran, and B K Moore

Indiana University School of Dentistry, Department of Restorative Dentistry, Indianapolis 46202-5186, USA.

This study compared the effects of different dentin surface treatments on the shear bond strengths of three adhesive systems. The adhesive systems included a resin-modified glass ionomer, Fuji II LC, and two dentin bonding systems, One Step and Scotchbond Multi-Purpose Plus. The surface treatments compared for each adhesive system were as follows: 1) the controls, which were conditioned, 2) air abrasion at 120 psi without conditioning, 3) air abrasion at 160 psi without conditioning, 4) air abrasion at 120 psi with conditioning, and 5) air abrasion at 160 psi with conditioning. The KCP 1000 Whisperjet was used for all air-abrasive specimens. Controls for each adhesive material (Fuji II LC, One Step, Scotchbond Multi-Purpose Plus) were bonded using manufacturers' recommendations. Results showed that air abrasion significantly lowered bond strength of the resin-modified glass ionomer, conditioned or nonconditioned (P < 0.01). Air abrasion alone significantly lowered bond strengths of the dentin bonding agent systems (P < 0.01). However, air abrasion plus conditioning of the dentin surface resulted in bond strengths that were similar to the conditioned-only specimens (P < 0.01).

UI	MeSH Term	Description	Entries
D008422	Materials Testing	The testing of materials and devices, especially those used for PROSTHESES AND IMPLANTS; SUTURES; TISSUE ADHESIVES; etc., for hardness, strength, durability, safety, efficacy, and biocompatibility.	Biocompatibility Testing,Biocompatible Materials Testing,Hemocompatibility Testing,Testing, Biocompatible Materials,Testing, Hemocompatible Materials,Hemocompatibility Testings,Hemocompatible Materials Testing,Materials Testing, Biocompatible,Materials Testing, Hemocompatible,Testing, Biocompatibility,Testing, Hemocompatibility,Testing, Materials,Testings, Biocompatibility
D008689	Methacrylates	Acrylic acids or acrylates which are substituted in the C-2 position with a methyl group.	Methacrylate
D012117	Resins, Synthetic	Polymers of high molecular weight which at some stage are capable of being molded and then harden to form useful components.	Dental Resins,Dental Resin,Resin, Dental,Resin, Synthetic,Resins, Dental,Synthetic Resin,Synthetic Resins
D001840	Dental Bonding	An adhesion procedure for orthodontic attachments, such as plastic DENTAL CROWNS. This process usually includes the application of an adhesive material (DENTAL CEMENTS) and letting it harden in-place by light or chemical curing.	Bonding, Dental,Cure of Orthodontic Adhesives,Curing, Dental Cement,Dental Cement Curing,Orthodontic Adhesives Cure
D005899	Glass Ionomer Cements	A polymer obtained by reacting polyacrylic acid with a special anion-leachable glass (alumino-silicate). The resulting cement is more durable and tougher than others in that the materials comprising the polymer backbone do not leach out.	Glass Ionomer Cement,Glass Polyalkenoate Cement,Polyalkenoate Cement,Polyalkenoate Cements,Glass Polyalkenoate Cements,Glass-Ionomer Cement,Cement, Glass Ionomer,Cement, Glass Polyalkenoate,Cement, Glass-Ionomer,Cement, Polyalkenoate,Cements, Glass Ionomer,Cements, Glass Polyalkenoate,Cements, Glass-Ionomer,Cements, Polyalkenoate,Glass-Ionomer Cements,Ionomer Cement, Glass,Polyalkenoate Cement, Glass
D006801	Humans	Members of the species Homo sapiens.	Homo sapiens,Man (Taxonomy),Human,Man, Modern,Modern Man
D000399	Air Pressure	The force per unit area that the air exerts on any surface in contact with it. Primarily used for articles pertaining to air pressure within a closed environment.	Air Pressures,Pressure, Air,Pressures, Air
D000537	Aluminum Oxide	An oxide of aluminum, occurring in nature as various minerals such as bauxite, corundum, etc. It is used as an adsorbent, desiccating agent, and catalyst, and in the manufacture of dental cements and refractories.	Alumina,Alumina Ceramic,Aluminum Oxide (Al130O40),Aluminum Oxide (Al2O),Aluminum Oxide (AlO2),Bauxite,Corundum,Sapphire,Ceramic, Alumina,Oxide, Aluminum
D000704	Analysis of Variance	A statistical technique that isolates and assesses the contributions of categorical independent variables to variation in the mean of a continuous dependent variable.	ANOVA,Analysis, Variance,Variance Analysis,Analyses, Variance,Variance Analyses
D013314	Stress, Mechanical	A purely physical condition which exists within any material because of strain or deformation by external forces or by non-uniform thermal expansion; expressed quantitatively in units of force per unit area.	Mechanical Stress,Mechanical Stresses,Stresses, Mechanical